Description
Silica carbide brick is a kind of refractory product mainly made of SiC, the silica carbide content is 72%~99%. Generally, add binding agent (or non-binding agent), made by the burdening, mixing, molding and burnt. The principal crystalline phase is SiC.

Description
Alumina Bubble Brick is a new type high temperature heating insulation materials and made of industrial alumina in the electrical furnace through smelting and blowing. Alumina Bubble Bricks’ crystal form is a-Al2O3 microcrystal and main body is alumina bubble that can be made to be all kinds of products with various shapes for serving the highest temperature of 1800℃ with high mechanic

Description
Lightweight clay insulating brick is made of high purity fire clay, by adding combustible, gas evolution method, or foam method. Lightweight clay brick is a kind of porous material with Al2O3 content 30-46%. Its refractoriness is 1580-1750 °C, refractoriness under load is 1250-1450 °C, with good thermal resistance and strong ability to resistant acid slag.

Description
High alumina brick with more than 48% Al2O3 content is a kind of neutral refractory. It is formed and calcined by bauxite or other high content of alumina raw materials. High thermal stability, fire resistance at 1770℃ and above. Good slag resistance, it is mainly used in the construction of electric furnace, glass furnace, cement rotary furnace and so on.

Lightweight clay insulating brick

Description
Fire clay brick is made of clay clinker as aggregate and refractory clay as binder, then make refractory material with Al2O3 content of 30%-48%.

Description
Magnesia-calcia-carbon brick with the choice of special calcium-based materials, resins and a special water proof treatment technique, Mg-CaO-C bricks for refining ladles. Mgo-Cao-C brick can absorb non-metal inclusions in the molten steel so as to purify the molten steel.

Description
Magnesia-calcia brick is made of two-step calcined MgO Cao sand and high-purity (electric melting or sintering) magnesia by high-pressure molding and high-temperature firing, vacuum pressure impregnation. It is a green product with good high-temperature creep and slag resistance.

Description
Magnesia chrome brick is made of high quality magnesia and chrome concentrate. The product has good high temperature resistance and strong thermal shock stability. It can be applied to the top of electric furnace, refining furnace outside furnace and various nonferrous metal smelting furnaces. In addition, the magnesia chrome brick is also suitable for the regenerator of cement rotary.